사출중량 is an important parameter of the injection molding machine. It is the most frequently used parameter when selecting an injection molding machine, expressed in ounces or grams. Although this parameter is simple and easy to understand, it is easy to be misunderstood. The reason is very simple. When the plastic is selected, the injection molder can determine the weight of the plastic part, so they can easily choose the machine by this injection weight. In fact, the injection weight is defined as the weight of the plastic injection when an empty injection (not injected into the mold) is measured, rather than theoretically calculated. The compound used is usually a general hard rubber with a specific gravity of 1.05. When the plastic of the plastic part is different from PS, the injection weight of the specification can be used after the following conversion. Injection weight of non-PS plastic = c*b/1.05, (b = specific gravity of plastic and c = injection weight expressed in PS.) For example: the specific gravity of Saigang is 1.42, it is in one injection weight (calculated as PS) 8 oz.

(1) 사출 중량이 충분한 사출 성형기를 선택하십시오. 사출 중량이 플라스틱 부품의 중량과 유동 채널 플라스틱의 중량을 더한 사출 성형기를 선택해서는 안됩니다. 장난감 초상화와 같이 덜 까다로운 사출 성형에서는 총 중량이 사출 중량의 85%가 되어야 합니다. 크리스탈 공급과 같은 까다로운 사출 성형에서는 75%입니다. 공사출에서 측정된 사출중량은 사출압력에서 작고, 고사출성형에는 높은 사출압력이 요구된다.

예를 들어 비중 1.38의 경질 폴리염화비닐(UPVC)을 사용하여 장난감 초상화를 성형하는 경우 플라스틱 부품과 러너 플라스틱의 무게는 4온스이므로 사출 성형기를 사출해야 합니다. PS = 4*1.05/0.38 =3.04 oz를 특징으로 하는 사출 중량. 85% 가이드를 사용하면 필요한 주입 주입 중량 = 3.04 / 0.85 = 3.58oz.

(2) 사출중량이 과도한 사출성형기를 사용해서는 안 된다. 플라스틱 부품과 러너 플라스틱의 총 중량은 사출 중량의 35%~85% 사이여야 합니다. 하한은 스텐실의 굽힘, 배럴 내 플라스틱의 체류 시간, 사출 성형 부품의 kg당 전력 소비 등 세 가지 고려 사항에 따라 결정됩니다.

작은 사출 성형 부품에 작은 금형을 사용하면 형판이 과도하게 구부러져 긁힐 수 있고(제품 품질에 영향을 미침) 심지어 형판이 파열될 수도 있습니다.

대형 사출 성형기로 작은 플라스틱 부품을 사출 성형할 때 용융물의 체류 시간이 너무 길면 플라스틱이 분해됩니다.

다중 캐비티 또는 더 큰 다이 크기를 사용하면 대형 기계로 작은 플라스틱 부품을 성형할 때 발생하는 문제 중 일부를 해결할 수 있습니다. 배럴의 온도를 낮추면 체류 시간이 길어져 스피치의 분해도 쉬워집니다.